Tools

LEADER 05256cam 2200541Ii 4500

001 ocn968303097;

003 OCoLC;

005 20170424101534.0;

006 m o d ;

007 cr unu||||||||;

008 170113s2016 ncua obm 000 0 eng d;

035 a| (Sirsi) o968303097;

035 a| (OCoLC)968303097;

049 a| EREE;

090 a| TP156.P6;

100 1 a| Vargas, Daniel E.,e| author.?| UNAUTHORIZED;

245 10 a| Poly(ethylene oxide)/[beta]-lactoglobulin electrospun nanofibers :b| chemical crossliking assessment and thymosin-[beta]4 functionalization /c| by Daniel E. Vargas.;

246 3 a| Poly(ethylene oxide)/[beta]-lactoglobulin electrospun nanofibers chemical crosslinking assessment and thymosin-[beta]4 functionalization.;

264 1 a| [Greenville, N.C.] :b| [East Carolina University],c| 2016.;

300 a| 80 pages :b| illustrations (chiefly color);

336 a| textb| txt2| rdacontent;

337 a| computerb| c2| rdamedia;

338 a| online resourceb| cr2| rdacarrier;

347 a| text fileb| PDFc| 1.06 MB2| rda;

538 a| System requirements: Adobe Reader.;

538 a| Mode of access: World Wide Web.;

502 b| M.S.c| East Carolina Universityd| 2016.;

500 a| Presented to the faculty of the Department of Engineering.;

500 a| Advisor: Barbara Muller-Borer.;

500 a| Title from PDF t.p. (viewed February 10, 2017).;

520 3 a| Using electrospun nanofiber scaffolds have emerged as a technique for tissue engineering (TE) applications. In 2011, Sullivan et al. reported on the process to effectively electrospin and crosslink nanofibers from poly(ethylene oxide) (PEO) and [beta]-lactoglobulin (BLG) aqueous solutions. PEO and BLG are both biodegradable and biocompatible materials. Crosslinking PEO/BLG nanofibers is necessary to improve their aqueous stability for TE applications. However, the heat treatment process suggested by Sullivan et al. is time intensive. The purpose of this study was to a) investigate an alternative crosslinking method for electrospun nanofibers made from an aqueous protein solution b) assess the resulting nanofibers for their potential use as scaffolds for TE applications, and c) evaluate the effect of biologically treated nanofiber scaffolds on stem cell proliferation. Chemical crosslinking techniques using Sodium Trimetaphosphate (STMP) combined with sodium hydroxide (NaOH) were evaluated. STMP has been shown to effectively crosslink polysaccharide nanofibers in situ during electrospinning. Methods: STMP, at various concentrations, was added to PEO/BLG electrospinning solutions. The effects of STMP were characterized by measuring the solution's viscosity, pH and conductivity. Confocal laser scanning microscopy (CLSM) images were acquired to qualitatively assess electrospun nanofiber morphology and scaffold topography. Human mesenchymal stem cells (hMSC) were grown on PEO/BLG scaffolds under control conditions and when treated with the protein Thymosin-[beta]4 (T[beta]4). HMSC proliferation was assessed to evaluate the effects of PEO/BLG nanofiber scaffolds and different T[beta]4 treatments at day 2, 4 and 8. Results: Using STMP to chemically crosslink PEO/BLG electrospun scaffolds affected solution properties, nanofiber morphology and scaffold topography. PEO/BLG/STMP nanofibers were highly beaded and wavy with little structure relative to PEO/BLG nanofibers. Fibers were not stable in an aqueous solution.Using T[beta]4 to treat the PEO/BLG nanofiber scaffolds and/or cell culture media improved hMSC proliferation with increased time in culture. HMSCs remained viable throughout the growth period for all treatments. However, hMSCs did not integrate into PEO/BLG nanofiber scaffolds, but attached to the scaffold surface. Conclusion: Using STMP, at the tested concentrations, as an alternative crosslinker for PEO/BLG nanofibers was ineffective and did not result in usable electrospun scaffolds. Chemically crosslinking PEO/BLG nanofibers requires further research in polymer chemistry to identify an alternative in situ crosslinking mechanism. Treating the scaffolds and/or media with T[beta]4 did result in improved hMSC proliferation. However, while hMSC cultures remained viable and proliferation increased with T[beta]4 treatments, further research is necessary to develop protocols that will enable hMSC integration with PEO/BLG nanofiber scaffolds.;

504 a| Includes bibliographical references.;

650 0 a| Crosslinking (Polymerization)=| ^A1012102;

650 0 a| Nanofibers.=| ^A786649;

650 0 a| Polyethylene oxide.=| ^A1036832;

650 0 a| Lactoglobulins.=| ^A1326520;

653 a| HMSC;

653 a| stem cells;

700 1 a| Muller-Borer, Barbara J.,e| degree supervisor.?| UNAUTHORIZED;

710 2 a| East Carolina University.b| Department of Engineering.=| ^A1231592;

856 40 z| Access via ScholarShipu| http://hdl.handle.net/10342/6044;

949 o| wjh;

994 a| C0b| ERE;

596 a| 1 4;

998 a| 4604957;

999 a| CLICK ON WEB ADDRESSw| ASISc| 1i| 4604957-1001l| JNETm| JOYNERr| Ys| Yt| JNE3ETDu| 1/13/2017x| ETDz| JERESOURCE;

999 a| CLICK ON WEB ADDRESSw| ASISc| 1i| 4604957-2001l| HSLELECm| HSLr| Ys| Yt| HEETDu| 1/13/2017x| ETDz| HERESOURCE;

Poly(ethylene oxide)/[beta]-lactoglobulin electrospun nanofibers : chemical crossliking assessment and thymosin-[beta]4 functionalization / by Daniel E. Vargas.

Author/creator	Vargas, Daniel E. author.
Other author	Muller-Borer, Barbara J., degree supervisor.
Other author	East Carolina University. Department of Engineering.
Format	Theses and dissertations
Publication	[Greenville, N.C.] : [East Carolina University], 2016.
Description	80 pages : illustrations (chiefly color)
Supplemental Content	Access via ScholarShip
Subjects	Crosslinking (Polymerization) Nanofibers. Polyethylene oxide. Lactoglobulins.

Variant title	Poly(ethylene oxide)/[beta]-lactoglobulin electrospun nanofibers chemical crosslinking assessment and thymosin-[beta]4 functionalization.
Summary	Using electrospun nanofiber scaffolds have emerged as a technique for tissue engineering (TE) applications. In 2011, Sullivan et al. reported on the process to effectively electrospin and crosslink nanofibers from poly(ethylene oxide) (PEO) and [beta]-lactoglobulin (BLG) aqueous solutions. PEO and BLG are both biodegradable and biocompatible materials. Crosslinking PEO/BLG nanofibers is necessary to improve their aqueous stability for TE applications. However, the heat treatment process suggested by Sullivan et al. is time intensive. The purpose of this study was to a) investigate an alternative crosslinking method for electrospun nanofibers made from an aqueous protein solution b) assess the resulting nanofibers for their potential use as scaffolds for TE applications, and c) evaluate the effect of biologically treated nanofiber scaffolds on stem cell proliferation. Chemical crosslinking techniques using Sodium Trimetaphosphate (STMP) combined with sodium hydroxide (NaOH) were evaluated. STMP has been shown to effectively crosslink polysaccharide nanofibers in situ during electrospinning. Methods: STMP, at various concentrations, was added to PEO/BLG electrospinning solutions. The effects of STMP were characterized by measuring the solution's viscosity, pH and conductivity. Confocal laser scanning microscopy (CLSM) images were acquired to qualitatively assess electrospun nanofiber morphology and scaffold topography. Human mesenchymal stem cells (hMSC) were grown on PEO/BLG scaffolds under control conditions and when treated with the protein Thymosin-[beta]4 (T[beta]4). HMSC proliferation was assessed to evaluate the effects of PEO/BLG nanofiber scaffolds and different T[beta]4 treatments at day 2, 4 and 8. Results: Using STMP to chemically crosslink PEO/BLG electrospun scaffolds affected solution properties, nanofiber morphology and scaffold topography. PEO/BLG/STMP nanofibers were highly beaded and wavy with little structure relative to PEO/BLG nanofibers. Fibers were not stable in an aqueous solution.Using T[beta]4 to treat the PEO/BLG nanofiber scaffolds and/or cell culture media improved hMSC proliferation with increased time in culture. HMSCs remained viable throughout the growth period for all treatments. However, hMSCs did not integrate into PEO/BLG nanofiber scaffolds, but attached to the scaffold surface. Conclusion: Using STMP, at the tested concentrations, as an alternative crosslinker for PEO/BLG nanofibers was ineffective and did not result in usable electrospun scaffolds. Chemically crosslinking PEO/BLG nanofibers requires further research in polymer chemistry to identify an alternative in situ crosslinking mechanism. Treating the scaffolds and/or media with T[beta]4 did result in improved hMSC proliferation. However, while hMSC cultures remained viable and proliferation increased with T[beta]4 treatments, further research is necessary to develop protocols that will enable hMSC integration with PEO/BLG nanofiber scaffolds.
General note	Presented to the faculty of the Department of Engineering.
General note	Advisor: Barbara Muller-Borer.
General note	Title from PDF t.p. (viewed February 10, 2017).
Dissertation note	M.S. East Carolina University 2016.
Bibliography note	Includes bibliographical references.
Technical details	System requirements: Adobe Reader.
Technical details	Mode of access: World Wide Web.

Availability

Library	Location	Call Number	Status	Item Actions
	Electronic Resources	Access Content Online	✔ Available

Poly(ethylene oxide)/[beta]-lactoglobulin electrospun nanofibers : chemical crossliking assessment and thymosin-[beta]4 functionalization / by Daniel E. Vargas.

Click here for more information about this title

Availability